Stainless Steel | Ferritic
1.4000 Sheet and Plate
Commercial410S
Grade 410S / 1.4000 ferritic stainless steel is a lower carbon version of grade 410.
Unlike the martensitic grade 410 this grade is NOT hardenable.
Chemical Composition
|
EN 10088-2:2005 1.4000 Steel |
|
|---|---|
| Chemical Element | % Present |
| Iron (Fe) | balance |
| Sulphur (S) | 0.02 max |
| Phosphorous (P) | 0.04 max |
| Carbon (C) | 0.08 max |
| Manganese (Mn) | 1 max |
| Silicon (Si) | 1 max |
| Chromium (Cr) | 12 - 14 |
Alloy Designations
Grade 1.4000 has similarities to the following grades but may not be a direct equivalent:
410S
1.4000
UNS S41008
403S17
Supplied Forms
- Plate
Generic Physical Properties
| Physical Property | Value |
|---|---|
| Density | 7.80 g/cm³ |
| Thermal Expansion | 9.9 x10^-6 /K |
| Modulus of Elasticity | 190-210 GPa |
| Thermal Conductivity | 24.9 W/m.K |
Mechanical Properties
|
EN 10088-2:2005 Sheet - Up to 8mm Thick |
|
|---|---|
| Mechanical Property | Value |
| Proof Stress | 240 Min MPa |
| Tensile Strength | 400 - 600 MPa |
| Elongation A | 19 Min % |
|
EN 10088-2:2005 Plate - Over 8mm up to 25mm Thick |
|
|---|---|
| Mechanical Property | Value |
| Proof Stress | 220 Min MPa |
| Tensile Strength | 400 - 600 MPa |
| Elongation A | 19 Min % |
Properties Shown above are for Sheet / Plate